Electrodes OZS-12

WELDING ELECTRODES OZS-12 (diameter: 2; 2,5; 3; 4; 5 mm)

CLASSIFICATION: E46 in accordance with GOST 9466-75

LEGEND:E46 - OZS-12 - Ø - UD
                      E 432 - P21

TECHNICAL REQUIREMENTS:GOST 9466-75, GOST 9467-75, TU BY 100034500.044-2013

COATING: rutile

PURPOSE:

Welding critical structures of carbon and low-alloy steels having a strength up to 490 MPa, when the formation of welding seams in different spatial positions are increased requirements. Ensure easy execution of the welding process, in Vol. C. In the overhead position and tack in the formulation, as well as orbital welding joints of pipelines. Small diameter electrodes can weld from the power supply included in the domestic network.

In all spatial positions of the weld, except vertical "downward", AC and DC forward and reverse polarity

CHARACTERISTICS Electrodes:

arcing

sustainable;

splashing degree

small

formation of the joint

good;

Separation of the slag crust

good

The tendency of the weld metal to pore formation

low;

deposition rate (in the lower position of the weld)

8.0-9.0 g / Ah;

deposition rate (electrode diameter 4.0 mm)

1,2-1,6 kg / h;

Electrode consumption per 1 kg of weld metal

1.7 kg;

Typical mechanical properties of weld metal (at 20 ° C):

Tensile strength, MPa

Yield strength, MPa

Relative extension, %

Impact toughness J / cm2

510

420

25

130

Chemical composition of deposited metal:

Element content,%

Carbon

Manganese

Silicon

Sulfur

Phosphorus

<= 0.12

0,45-0,80

0.10-0.25

<= 0.030

<= 0.035

DIRECTIONS FOR USE:

In case of exceeding the permissible moisture content in the coating (1.5%) before use further electrodes are calcined at a temperature of 150-170 ° C for 30-60 minutes.

WELDING MODES:

Electrode diameter mm

Welding current, A

joint position

Underwear

vertical

ceiling

2.0

50-80

40-60

40-60

2.5

60-90

50-80

50-80

3

70-110

60-90

60-90

4

120-150

100-140

100-140

5

130-180

120-170

-


Welding the lower position to produce elevated modes electrode tilt toward the direction of welding (back angle). It recommended average arc length.