Electrodes ANO - 36

WELDING ELECTRODES ANO - 36 (diameter 2; 2,5; 3; 4; 5 mm)

CLASSIFICATION: E46 GOST 9466-75, GOST 9467-75 and TU RB 100034500.017-2006;

LEGEND: E46 - ELN-36 - Ø - UD
                     E 432 (3) - RTS13

TECHNICAL REQUIREMENTS: GOST 9466-75, GOST 9467-75 and TU RB 100034500.017-2006;

COATING: rutile - cellulose;

PURPOSE:

Intended for welding ordinary and critical structures of carbon steels according to GOST 380-94 GOST 1050-88 and all degrees of deoxidation, in all positions seam alternating current and direct current reverse polarity.

CHARACTERISTICS Electrodes:

arcing

sustainable;

The degree of spattering,%

Minor;

formation of the joint

good;

Separation of the slag crust

good;

The tendency of the weld metal to pore formation

low;

deposition rate (in the lower position of the weld)

8.0-9.0 g / Ah;

deposition rate (electrode diameter 4.0 mm)

1,2-1,6 kg / h;

Electrode consumption per 1 kg of weld metal

1.7 kg;

Typical mechanical properties all weld metal (at normal temperature)

Tensile strength, MPa

Relative extension, %

Impact toughness J / cm2

460

22

80

Chemical composition of deposited metal:

Element content, weight%

Carbon

Silicon

Manganese

Sulfur

Phosphorus


No more than 0.12

0,10-0,50

0,4-0,85

No more

0,040

0,045

DIRECTIONS FOR USE:

In case of exceeding the permissible moisture content in the coating (2.5%) before use further electrodes are calcined at a temperature of 110-130 oc. Within 30 minutes.

WELDING MODES:

Electrode diameter mm

Welding current, A

joint position

Underwear

vertical

ceiling

2.0

50-80

40-60

40-60

2.5

60-90

50-80

50-80

3

90-110

80-100

80-100

4

120-150

100-140

100-140

5

130-180

120-170

140-190

Welding vertical joints manner "top down" made a short arc or journalled. Do not allow the slag flowing ahead of the arc. For this purpose the angle of 40-70 to the vertical axes. Downhand recommended tilted in the direction of the welding axes 20-40 of the vertical.